etfe 210流动性高, 薄壁部件etfe,连接器etfe

 

Tefzel 210
乙烯四氟乙烯共聚物
DuPont Fluoropolymers

产品说明

DuPont™ Tefzel ® fluoropolymer 210 is a specialpurpose resin available in translucent, 2.5-mm (0.1-in) pellets. Compared to other grades of Tefzel ®, it has a higher flow rate and a lower maximum service temperature.

Tefzel ® 210 and the other Tefzel ® fluoropolymers are melt processible, modified copolymers of ethylene and tetrafluoroethylene. They are high-performance resins that can be processed at relatively high rates compared to fluorocarbon resins. They are mechanically tough and offer an excellent balance of properties.

The relatively high flow rate of Tefzel ® 210 makes it uniquely suitable for high speed processing, especially for extruded coatings and injection molding of slender, thin-walled or intricate shapes. Molded or extruded products made from Tefzel ® 210 are preferred for uses that do not involve significant flexural or tensile stress at elevated temperatures.

Properly processed products made from virgin Tefzel ® 210 are inert to most solvents and chemicals, hydrolytically stable and weather resistant. Recommended upper service temperature is 135°C (275°F); useful properties are retained at cryogenic ranges. The level and stability of dielectric properties are excellent and the flame rating is V-0 by the UL94 method. Mechanical properties include outstanding impact strength, cut-through and abrasion resistance.

Statements, or data, regarding behavior in a flame situation are not intended to reflect hazards presented by this or any other material when under actual fire conditions.

总体

材料状态 • 已商用:当前有效   
供货地区 • 北美洲 • 欧洲  
 • 南美洲 • 亚太地区  
    
 • 抗溶解性 • 耐化学性良好 • 韧性良好 
性能特点 • 抗撞击性,良好 • 耐磨蚀性,良好  
   • 水解稳定 
 • 流动性高 • 耐气候影响性能良好  
    
 • 薄壁部件 • 管道 • 容器 
用途 • 电气/电子应用领域 • 紧固件  
   • 实验室器具 
 • 阀门/阀门部件 • 连接器  
    
外观 • 半透明   
形式 • 颗粒料   
加工方法 • 吹塑成型 • 挤压层涂法 • 注射成型 
 • 挤出 • 压缩模塑  
    
    
物理性能  额定值单位制 测试方法 
比重  1.70g/cm³ ASTM D792 
熔流率 (297°C/5.0 kg)  20g/10 min ASTM D1238 
吸水率 (24 hr)  0.0070% ASTM D570 
机械性能  额定值单位制 测试方法 
抗张强度 (23°C)  40.0MPa ASTM D638 
伸长率 (断裂, 23°C)  300% ASTM D638 
弯曲模量 (23°C)  1170MPa ASTM D790 
压缩强度  37.9MPa ASTM D695 
冲击性能  额定值单位制 测试方法 
悬壁梁缺口冲击强度 (23°C)  无断裂 ASTM D256 
硬度  额定值单位制 测试方法 
硬度计硬度 (邵氏 D)  63 ASTM D2240 
热性能  额定值单位制 测试方法 
熔融温度  255 到 280°C  
线形膨胀系数 - 流动 (0 到 100°C)  0.00013cm/cm/°C ASTM D696 
电气性能  额定值单位制 测试方法 
体积电阻率  1.0E+17ohm•cm ASTM D257 
介电强度 (0.254 mm)  71kV/mm ASTM D149 
介电常数 (23°C, 1 MHz)  2.55 ASTM D150 
耗散因数 (23°C, 1 MHz)  0.0054 ASTM D150 
耐电弧性  122sec ASTM D495 
可燃性  额定值单位制 测试方法 
极限氧指数  31% ASTM D2863