PTFE HGR203

 

China PPS PTFE-hGR203
聚苯硫醚
Sichuan Deyang Chemical Co., Ltd

产品说明

PPS/PTFE-hGR203 is lubricant PPS compound, which is filled with glass fiber, PTFE and ingredients based on the PPS resin. It shows solvent resistance, abrasive resistance and good mechanic prosperity, high modulus, creep resistance, high-temperature resistance, inherent flame resistance, easy processing, low mold shrinkage, good dimensional stability.

Owing to its high performance, it's widely used in mechanical and chemical industry for making wearable parts/components which work in the high-temperature, high pressure and solvent circumstance. Such as: plastic axle bearing, axle sleeve, textile machine components, components which are used in aero industry.

总体

材料状态 • 已商用:当前有效  
供货地区 • 亚太地区  
填料/增强材料 • 玻璃纤维增强材料  
添加剂 • PTFE润滑剂  
 • 尺寸稳定性良好 • 可加工性,良好 • 耐热性,高
性能特点 • 经润滑 • 耐磨蚀性,良好 • 收缩性低
 • 抗溶解性 • 耐磨损性良好 • 阻燃性能
用途 • 工业领域: • 航空航天应用 • 医疗/护理领域的应用
加工方法 • 注射成型  

物理性能 额定值单位制 测试方法
密度 1.52g/cm³ Internal Method
收缩率 - 流动 0.25% Internal Method
机械性能 额定值单位制 测试方法
抗张强度 126MPa Internal Method
伸长率 (断裂) 1.8% Internal Method
弯曲模量 8500MPa Internal Method
弯曲强度 174MPa Internal Method
摩擦系数 0.37 Internal Method
Abrasion - Width 6mm Internal Method
磨损量 2 4.5mg Internal Method
冲击性能 额定值单位制 测试方法
悬壁梁缺口冲击强度 11kJ/m² Internal Method
硬度 额定值单位制 测试方法
洛氏硬度 3 104 Internal Method
热性能 额定值单位制 测试方法
热变形温度 (1.8 MPa, 未退火) 266°C Internal Method
熔融温度 281°C Internal Method
可燃性 额定值单位制 测试方法
UL 阻燃等级 V-0 Internal Method
  
注射 额定值单位制 
干燥温度 110 到 140°C 
干燥时间 3.0 到 5.0hr 
螺筒后部温度 270 到 290°C 
螺筒中部温度 300 到 320°C 
螺筒前部温度 300 到 320°C 
射嘴温度 290 到 320°C 
加工(熔体)温度 160°C 
模具温度 100 到 150°C 
注塑温度 50.0 到 100MPa 
背压 0.100 到 1.00MPa 
螺杆转速 40 到 100rpm 
注射说明  
Processing time: 2 to 8hr  
1 / 2  
  
  
  
  
  
 
China PPS PTFE-hGR203 2012年9月29日
聚苯硫醚
Sichuan Deyang Chemical Co., Ltd
备注
1 一般属性:这些不能被视为规格。

2 120 min

3 HR

 

 

 

 

 

 

 

 

 

 

 

 

 

 

 

 

 

 

 

 

 

 

 

 

 

 

 

 