内容编辑

Shanghai Ofluorine PVDF M-1
聚偏二氟乙烯
Shanghai Ofluorine Chemical Technology Co., Ltd

产品说明
M-1 PVDF is a kind of granules homopolymer, which has high melt viscosity, M-1 is more suitable for compression moulding process.
M-1 PVDF pellets as raw materials, the finished products has excellent mechanical strength and tenacity. It can not be eroded by acid, alkali, strong oxidant, halogens. Good durability to aliphatic hydrocarbons, aromatic hydrocarbons, alcohol, aldehyde etc. In the work ofhydrochloric acid, nitric acid, sulfuric acid, dilute alkali liquor, dense alkali liquor(40%) and 100°C temperature, its performance keep stable.

Others, M-1 PVDF finished products has the properties of X-Ray resistant, UV resistant, andstability in wide temperature range.

总体

材料状态 • 已商用：当前有效  
供货地区 • 亚太地区  
 • 高强度 • 抗紫外线性能良好 • 气味低到无
性能特点 • 均聚物 • 耐化学性良好 • 热稳定性，良好
 • 抗辐射性 • 耐用性 • 粘度，高
外观 • 半透明  
形式 • 颗粒  
加工方法 • 压缩模塑  

物理性能 额定值单位制 测试方法
比重 1.77 到 1.79g/cm³ ASTM D792
熔流率 (230°C/10.0 kg) 1.0 到 4.0g/10 min ASTM D1238
吸水率 (饱和) < 0.050% ASTM D570
机械性能 额定值单位制 测试方法
抗张强度 2  ASTM D638
屈服, 23°C > 40.0MPa 
断裂, 23°C > 30.0MPa 
伸长率 2  ASTM D638
屈服, 23°C 5.0 到 10% 
断裂, 23°C > 20% 
硬度 额定值单位制 测试方法
硬度计硬度 (邵氏 D) 70 到 80 ASTM D2240
热性能 额定值单位制 测试方法
熔融峰值温度 3 165 到 171°C ASTM D3418
可燃性 额定值单位制 测试方法
UL 阻燃等级 V-0 UL 94

备注
1 一般属性：这些不能被视为规格。

2 50 mm/min

3 10°C/min